How well modified wood products perform may be influenced by their chemical compositions. Wood extractives are nonstructural constituents, many with specific biological properties, which affect the color, fragrance, hygroscopicity, durability, and acoustic properties and the drying and adhesion processes of wood. However, incomplete information is available on the extraction techniques and potential use of extractives as value-added chemical products. The main goal of this research was to explore the effects of thermo-vacuum treatment of Deodar cedar (
In the last decade several research groups have developed heat-treatment processes to create wood that would be suitable for industrial application. Heat treatment is an effective method to improve wood properties (
Many changes of wood properties are related to modifying of the wood’s physical and chemical compositions. Heating alters the microstructure and cell-wall components of wood, among other changes. Chemical modifications begin with the deacetylation of hemicelluloses followed by depolymerization, which leads to low-mass extractable compounds (
Extractives represent the nonstructural chemical components of plants. They are mainly produced in the heartwood in response to environmental stress (
Extractives can be drawn from wood by different approaches, and specific methods have been applied to influence the yield and type of extracted compound. Currently, the most commonly used extraction techniques require either the Soxhlet apparatus with solvents or autoclaving with hot water as a simple green method. Extractives are generally classified as water-soluble, toluene-ethanol-soluble, or ether-soluble, according to the extractive solvent. The amount of extractive compound dissolved in each solvent will differ, and the choice of the appropriate solvent will depend on the application. Organic solvents are able to extract resin compounds, whereas cold and hot water are useful to extract phenolic compounds, carbohydrates, glycosides, and soluble salts.
Promising evidence from experimental studies has highlighted that different nonpolar and polar solvents can be used to isolate different types of extractives from woods (
Boards (50 × 6 × 180 mm) of alder and cedar woods were dried under vacuum to a moisture content of 0%. Wood samples were firstly dried for 4 h in vacuum conditions (185-200 mbar) at a temperature of 90 °C. Then, thermal treatment was done at 200 °C for 4 h in a thermo-vacuum cylinder (WDE-Maspell s.r.l., Italy). Further information on the technology can be found in
Treated and untreated wood samples were powdered and extracted in a Soxhlet apparatus by using the TAPPI test method T204 (
For extraction, the Soxhlet apparatus was used with 300 ml of a 2:1 mixture of benzene: ethanol and 1 g of milled wood for 7 h. One gram of milled wood was sequentially extracted by solvents with increasing polarity (hexane < dichloromethane < methanol) for 7 h per solvent. The extraction apparatus consisted of a 500-ml flask, Soxhlet tube, and 300-mm Allihn condenser. Samples were put in cellulose thimbles (33 × 80 mm) of medium porosity. After extraction, the solution was dried in a previously weighed 25-ml flask, by using a rotary evaporator connected to a vacuum pump (Vacuumbrand PC3001). Extraction percentage was obtained by weighing the flask containing the residue and comparing the weight to that of the initial wood. The weight of each dried extract was measured by using a Gibertini E42 analytical balance (precision ± 0.1 mg).
Treated and untreated wood samples were split into small pieces and extracted with water as solvent in a Vapor Matic 770 sterilization autoclave. This completely automatic and thermoregulated autoclave system is equipped with a microprocessor, which permits time and temperature programming. The following autoclave cycle was used: 121 °C, 1 atm, 20 min. At the end of the process, the solution was dried by a lyophilization. The extraction percentage was calculated as described above.
GC-MS analyses were performed on an HP 6890 GC system equipped with an HP 5963 MS selective detector, with a high-temperature capillary column (HP-5MS, 30 m × 0.25 mm I.D., 0.25-μm film thickness; J&W Scientific, CA, USA) and helium as carrier gas. Samples were injected directly into the column at a temperature of 80 °C. After injection, the temperature was held at 80 °C for 3 min, and then heated to 250 °C at a rate of 20 °C min-1 and held for 20 min. Compounds were identified by computer comparison of the mass spectra with NIST libraries and by mass fragmentation patterns.
Amounts of extracts obtained from alder wood by any solvent, excluding benzene/ethanol, were smaller for untreated than for thermo-treated wood (
For both untreated wood species, greater amounts of extracts were obtained by the benzene/ethanol blend than by solvents with different polarities.
Larger amounts of polar extracts were obtained with the methanol solvent for thermo-treated wood (
Tab. S1 (Supplementary material) summarizes characteristics of the GC-MS peaks of untreated and thermo-treated alder wood samples subjected to different techniques and solvents. Differences in the chemical compositions of extracts obtained from untreated
Different results were obtained from consecutive extractions of untreated
We observed differences among the results in the classes of extracts obtained (row in bold, Tab. S1 in Supplementary material). Alkene compounds were obtained from untreated samples by using the Soxhlet apparatus. When using the water technique, alkenes were obtained only from thermo-treated samples. Extraction of untreated samples by methanol and benzene/ethanol resulted in extracts with longer aliphatic chains. Both dichloromethane and benzene/ethanol solvent yielded higher amounts of carbonyl and phenolic compounds from thermo-treated samples. These compounds could have resulted from the decomposition of volatile organic compounds (VOCs), terpenes, polyosides, and lignins (
Fatty acids were generally extracted from untreated wood by using hexane and methanol. However, with water and the benzene/ethanol mixture, fatty-acid derivatives (octadecanoic acid and 1-methylethyl dodecanoate, glycerol 1.2-diacetate, respectively) were extracted from thermo-treated samples. Octadecanoic acid is a saturated fatty acid, which may have resulted from the hydrolysis or degradation of fatty acids during heat treatment.
Building blocks of some wood structural components were obtained only after thermo-treatment, excluding diphenyldisulfide, extracted from untreated wood with methanol. Most of building block were obtained when using dichloromethane as solvent. No building block were obtained when using hexane as solvent. These compounds could derive from the thermal degradation of other structural components of wood.
Among the extracts from heat-treated alder, vanillin is an important extract that was obtained by the benzene/ethanol mixture. Vanillin is commonly employed in the biological and biotechnological industries as a flavoring agent in foods and pharmaceuticals products and as a fragrance in perfumes. According to
Tab. S2 (Supplementary material) summarizes the characteristics of the GC-MS peaks of untreated and thermo-treated cedar wood subjected to different techniques and solvents. In contrast to alder, cedar produced many similar extractive compounds from both untreated and thermo-treated samples. This finding suggests that cedar is more heat resistant and less degradable when subjected to heating. We were able to identify predominant compounds from thermo-treated
Acids and esters were extracted from cedar mainly by using water or the benzene/ethanol mixture with thermo-treated samples (row in bold, Tab. S2). While benzenepropanoic acid, 3.5-bis(1.1-dimethylethyl)-4-hydroxy-methyl ester (methanol), bis(2-ethylhexyl) phthalate, and isobutyl-octyl phthalate (hexane) were extracted from untreated samples. Alkene or alkene-like compounds were found in all extracts from cedar, regardless of heat treatment or solvent. Alkenes were most abundantly extracted when using benzene/ethanol with untreated and thermo-treated samples, or using water with thermo-treated samples.
Surprisingly, we found that long-chain compounds were extracted from thermo-treated samples. These extracts could be a building block component of the wood and not derived from thermal degradation or other alkenes.
Carbonyl compounds were obtained when thermo-treated samples were extracted with water, while phenylbenzeneacetic acid, methyl ester were obtained from untreated sample. Fatty acids were obtained only with water. Two different saturated fatty acids were obtained from untreated
Compounds belonging to the organic building block class were obtained when thermo-treated samples were extracted with water, hexane, dichloromethane, or methanol. For untreated samples, 3.5-dimethoxy-4-hydroxycinnamaldehyde was extracted by using water, and diphenyldisulfide was extracted by using methanol.
Some potentially valuable bioactive compounds were extracted from thermo-treated samples. For example, the terpene artumerone was extracted from thermo-treated samples by using hexane and dichloromethane solvents. Artumerone is a compound found in curcumin, a perennial plant cultivated throughout tropical Asia, India, and China. This compound has been investigated in clinical trials for its potential therapeutic properties, including anticancer activity (
This paper describes the analysis of compounds extracted from untreated and thermo-treated alder and cedar woods, by using polar and nonpolar solvents. The processes applied, wood material, and equipment used all affect the species and amounts of extracts. We also found that for both wood species the extractive composition was strongly related to the polarity of the extractive solvent.
The preliminary results showed that different types of polyaromatic compounds were produced from thermo-treated woods, with some difference between species, which was probably due to their different wood structures and thermal reaction rates.
Higher quantities of extracts were obtained from thermo-treated than from untreated alder wood samples, whereas the amounts of extracts obtained from untreated cedar wood were greater than those obtained from treated wood aside from methanol. For cedar, cross-linking probably takes place after polycondensation reactions between the chemical components of wood, which makes it difficult to obtain extractives.
For both alder and cedar, lower total percentages of compounds could be identified from untreated
Different compounds were extracted from treated
Extracts obtained from alder wood predominantly belonged to the acid/ester class, whereas extracts from cedar wood mostly belonged to the terpene and hydrocarbon classes.
We found many extracts that might have industrial applications as antimicrobial and antifungal agents or as important precursors in the manufacture of other aromatic compounds. Appropriate solvent selection is crucial for the extraction process and will depend on the intended application. To understand the appropriate procedure, a detailed analysis should be done that considers the chemical properties and final uses of the extracts, as well as the structural differences between wood species.
The authors would like to acknowledge the contribution of the COST Action FP1407. The Ph.D. program in “Agricultural, Forest and Food Science” at the University of Basilicata, supported T. Lovaglio.
Fragmentation of unidentified extractive compound.
Extraction yield in percentage (%) for untreated (C) and thermo-treated (TH) wood species.
Extraction Method | Italian alder | Deodar cedar | ||
---|---|---|---|---|
C | TH | C | TH | |
Water | 0.8 | 1.6 | 2.9 | 1.5 |
Hexane | 0.5 | 0.8 | 2.6 | 1.0 |
Dichloromethane | 0.5 | 1.3 | 1.3 | 1.0 |
Methanol | 4.5 | 7.1 | 3.4 | 4.8 |
Benzene/Ethanol | 8.2 | 2.2 | 10.8 | 9.0 |
Tab. S1 - Fraction A (Area %) of extracts and other compounds assessed by GC-MS analysis of samples of untreated (C) and thermo-treated (TH) alder.
Tab. S2 - Fraction A (Area %) of extracts and other compounds assessed by GC-MS analysis of samples of untreated (C) and thermo-treated (TH) cedar.